Полиэилентерефталат.
Органическим растворителем имеется ввиду
Спрашивал про поликарбонат, теперь другая проблема.
Можно ли растворить ПЭТ
в дмфа растворяется только относительно низкомолекулярный пэт.для обычно применяемого из головы могу назвать смесь фенола и тетрахлорэтана о-хлорфенол дихлоруксусная кислота или горячий трикрезол.впрочем в горячем феноле или хлороформе тоже растворится.а вообще заниматься этим не рекомендую.уж больно воняет
Polymers - A Property Database (CRC Press):
Soluble: phenol, chlorophenol, chlorobenzene, dichloroethane. Insoluble: hexane, C6H6, EtOH, cyclohexane
Encyclopedia of Polymer Science & Technology (Wiley):
As a step-growth polymer made under equilibration conditions, PET has a molecular weight distribution very close to the theoretical value of 2.0. The Mark–Houwink equation relates the intrinsic solution viscosity [] to the molecular weight as [] = KMv, where Mv is the viscosity average molecular weight and K and are the Mark–Houwink coefficients determined experimentally for individual solvents. The usual solvents historically used for PET are 60/40 w/w phenol/tetrachlorethane (P/TCE) and 2-chlorophenol (OCP). Neither solvent system is entirely satisfactory and better results have been obtained using either hexafluoroisopropyl alcohol (HFIP) or a 50/50 v/v mixture of HFIP and pentafluorophenol (PFP) at 25°C (63). Although expensive, these acidic fluorinated solvents readily dissolve even highly crystalline samples of PET at moderate temperatures, thus avoiding the degradation problems commonly encountered with the older solvents at high temperatures. Thus the results are more likely to be reliable, since degradation under normal conditions is minimal.
Soluble: phenol, chlorophenol, chlorobenzene, dichloroethane. Insoluble: hexane, C6H6, EtOH, cyclohexane
Encyclopedia of Polymer Science & Technology (Wiley):
As a step-growth polymer made under equilibration conditions, PET has a molecular weight distribution very close to the theoretical value of 2.0. The Mark–Houwink equation relates the intrinsic solution viscosity [] to the molecular weight as [] = KMv, where Mv is the viscosity average molecular weight and K and are the Mark–Houwink coefficients determined experimentally for individual solvents. The usual solvents historically used for PET are 60/40 w/w phenol/tetrachlorethane (P/TCE) and 2-chlorophenol (OCP). Neither solvent system is entirely satisfactory and better results have been obtained using either hexafluoroisopropyl alcohol (HFIP) or a 50/50 v/v mixture of HFIP and pentafluorophenol (PFP) at 25°C (63). Although expensive, these acidic fluorinated solvents readily dissolve even highly crystalline samples of PET at moderate temperatures, thus avoiding the degradation problems commonly encountered with the older solvents at high temperatures. Thus the results are more likely to be reliable, since degradation under normal conditions is minimal.
И серняга конц. даже без нагрева, а если разбавить раствор то выпадает, думаю полимер.Iskander писал(а):В ДМФА точно не растворится. Даже при кипячении.
К вышеописанным смесям могу добавить ещё диэтилфталат. При нагревании он там растворяется, при охлаждении падает. Вот только как бы это не под давлением делается...
А по простому - гидразин или крепкая щёлочь. Растворится без остатка
.Panteley писал(а):Есть достоверные сведения, что магнитофонную пленку хорошо склеивает муравьиная кислота. Значит ли зто, что она растваряет лавсановую основу (тот же ПЭТ) Может у кого есть возможность проверить? И что в итоге получится ? Может раствор мономера?
Почитай это , кстати пишут про два типы ПЕТа.